Stainless Steel Powder for Sintering Parts |
We adopt the best refining process to make the ingredients matched and more uniform.Compressibility, compactibility and green density can achieve the best results in a stable condition on the basis of our rich experience in mixing additives.
|
Material | Cr | Ni | Mo | Sn | Cu | S | P | C | O | N | Si | Mn | Fe | MPIF35 NO: |
Austenite Type |
303L | 17-19 | 8-13 |
| / | / | 0.15-0.30 | ≤0.2 | ≤0.03 | 0.1-0.2 | 0.02-0.03 | ≤1 | ≤0.5 | Bai | SS-303L |
304L | 18-20 | 8/12 | / | / | / | ≤0.03 | ≤0.03 | ≤0.03 | 0.1-0.2 | 0.02-0.03 | ≤1 | ≤0.3 | Bai | SS-304H, L |
316L | 16-18 | 10-14 | 2-3 | / | / | ≤0.03 | ≤0.03 | ≤0.03 | 0.1-0.2 | 0.02-0.03 | ≤1 | ≤0.3 | Bai | SS-316H, L |
317L | 18-21 | 12-16 | 3-4 | / | / | ≤0.03 | ≤0.03 | ≤0.03 | 0.1-0.2 | 0.02-0.03 | ≤1 | ≤0.3 | Bai | / |
310 | 24-26 | 19-22 | / | / | / | ≤0.03 | ≤0.3 | ≤0.08 | 0.1-0.2 | 0.02-0.03 | ≤1 | ≤0.3 | Bai | / |
303LSC | 17-19 | 8-13 | / | 1 | 4 | 0.15-0.30 | ≤0.2 | ≤0.03 | 0.1-0.2 | 0.02-0.03 | ≤1 | ≤0.3 | Bai | / |
304LSC | 17-19 | 8-13 | / | 1 | 4 | ≤0.03 | ≤0.03 | ≤0.03 | 0.1-0.2 | 0.02-0.03 | ≤1 | ≤0.3 | Bai | / |
316LSC | 16-19 | 10-14 | 2-3 | 1 | 4 | ≤0.03 | ≤0.03 | ≤0.03 | 0.1-0.2 | 0.02-0.03 | ≤1 | ≤0.3 | Bai | / |
Martensite Type |
410L | 11.5-13.5 | / | / | / | / | ≤0.03 | ≤0.03 | ≤0.03 | 0.1-0.2 | 0.02-0.03 | ≤1 | ≤0.3 | Bai | SS-410L |
Ferrite Type |
430L | 16-18 | / | / | / | / | ≤0.03 | ≤0.03 | ≤0.03 | 0.1-0.2 | 0.02-0.03 | ≤1 | ≤0.3 | Bai | SS-430L |
434L | 16-18 | / | 0.75-1.25 | / | / | ≤0.03 | ≤0.03 | ≤0.03 | 0.1-0.2 | 0.02-0.03 | ≤1 | ≤0.3 | Bai | SS—434L |
420 | 12-14 | / | / | / | / | ≤0.03 | ≤0.03 | 0.25-0.35 | 0.1-0.2 | 0.02-0.03 | ≤1 | ≤0.3 | Bai | / |
440 | 16-18 | / | / | / | / | ≤0.03 | ≤0.03 | 0.9-1.2 | 0.1-0.2 | 0.02-0.03 | ≤1 | ≤0.3 | Bai | / |
Martensite Precipitation Hardening Type |
17-4PH | 15.5-17.5 | 3-5 | Nb:0.15 |
| 3-5 | ≤0.03 | ≤0.03 | ≤0.07 | 0.1-0.2 | 0.02-0.03 | ≤1 | ≤0.3 | Bai | / |
Packing | In 25 kg plastic drums, 1000kg big plastic bags, as request |